27 December 2001 In-situ biaxial texture analysis of MgO films during growth on amorphous substrates by ion-beam-assisted deposition
Rhett Brewer, Paul N. Arendt, James R. Groves, Harry A. Atwater
Author Affiliations +
Abstract
We used a kinematical electron scattering model to develop a RHEED based method for performing quantitative analysis of mosaic polycrystalline thin film in-plane and out-of-plain grain orientation distributions. RHEED based biaxial texture measurements are compared to x-ray and transmission electron microscopy measurements to establish the validity of the RHEED analysis method. MgO was grown on amorphous Si3N4 by ion beam-assisted deposition (IBAD) using 750 eV Ar+ ions and MgO e-beam evaporation. The ion/MgO flux ratio was varied between 0.66 and 0.42. In situ RHEED analysis reveals that during nucleation the out-of-plane orientation distribution is very broad (almost random), but narrows very quickly once well-oriented grains reach a critical size. Under optimal conditions a competition between selective sputtering and surface roughening yields a minimum out-of-plane texture at about 100 angstrom, which degrades with increasing film thickness. The narrowest in- plane orientation distribution (5.4 degrees FWHM) was found to be at an ion/MgO flux ratio between 0.55 and 0.51, in good agreement with previous experiments. The systematic offsets between RHEED analysis and x-ray measurements of biaxial texture, coupled with evidence that biaxial texture improves with increasing film thickness, indicates that RHEED is a superior technique for probing surface biaxial texture.
© (2001) COPYRIGHT Society of Photo-Optical Instrumentation Engineers (SPIE). Downloading of the abstract is permitted for personal use only.
Rhett Brewer, Paul N. Arendt, James R. Groves, and Harry A. Atwater "In-situ biaxial texture analysis of MgO films during growth on amorphous substrates by ion-beam-assisted deposition", Proc. SPIE 4468, Engineering Thin Films with Ion Beams, Nanoscale Diagnostics, and Molecular Manufacturing, (27 December 2001); https://doi.org/10.1117/12.452547
Lens.org Logo
CITATIONS
Cited by 3 scholarly publications.
Advertisement
Advertisement
RIGHTS & PERMISSIONS
Get copyright permission  Get copyright permission on Copyright Marketplace
KEYWORDS
Ions

Transmission electron microscopy

X-rays

Homoepitaxy

X-ray diffraction

Diffraction

Crystals

RELATED CONTENT


Back to Top