Diameter distribution of thermally evaporated indium metal islands on silicon substrates

Joleyn Balch; Loucas Tsakalakos; William Huber; James Grande; Michael Knussman; Timothy S. Cale

doi:10.1117/12.752593

11 October 2007 Diameter distribution of thermally evaporated indium metal islands on silicon substrates

Joleyn Balch, Loucas Tsakalakos, William Huber, James Grande, Michael Knussman, Timothy S. Cale

Proceedings Volume 6768, Nanomaterials Synthesis, Interfacing, and Integrating in Devices, Circuits, and Systems II; 67680A (2007) https://doi.org/10.1117/12.752593
Event: Optics East, 2007, Boston, MA, United States

Abstract

Although many groups have studied the initial growth stages of various metals, including indium, there is little information in literature on diameter distributions of indium in relation to film thickness or annealing conditions. This paper reports island size distributions of thermally evaporated In islands on Si (100) and Si (111) substrates for nominal film thicknesses ranging from 5 to 50 nm. Because indium has a low melting temperature, and therefore a high homologous temperature at room temperature, 3-dimensional islands form during deposition with no subsequent heat treatments needed. Island diameters were calculated using commercial image analysis software in conjunction with SEM images of the samples. It is found that there is a bimodal island diameter distribution for nominal indium thicknesses greater than 5 nm. While the diameters of the larger islands increase exponentially with nominal thickness, those of the smaller islands increase linearly, and therefore more slowly, with nominal thickness. For nominal thickness of 50 nm, the average diameters of the small and large islands differ by almost an order of magnitude. Anneal conditions were studied in an attempt to narrow diameter distributions. Samples of each nominal thickness were annealed at temperatures ranging from 360°C to 550°C and the diameters again measured. The range of island diameters become narrower with 360°C anneal and volume average island diameter increases by ~30-50%. This narrowing of the distribution occurs due to smaller islands being absorbed by the larger in a process akin to Ostwald ripening, which is facilitated by higher surface diffusivities at higher homologous temperatures.

Citation Download Citation

Joleyn Balch, Loucas Tsakalakos, William Huber, James Grande, Michael Knussman, and Timothy S. Cale "Diameter distribution of thermally evaporated indium metal islands on silicon substrates", Proc. SPIE 6768, Nanomaterials Synthesis, Interfacing, and Integrating in Devices, Circuits, and Systems II, 67680A (11 October 2007); https://doi.org/10.1117/12.752593

ACCESS THE FULL ARTICLE

INSTITUTIONAL
Select your institution to access the SPIE Digital Library.

SELECT YOUR INSTITUTION

PERSONAL
Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.

PERSONAL SIGN IN

No SPIE Account? Create one

PURCHASE THIS CONTENT

SUBSCRIBE TO DIGITAL LIBRARY

50 downloads per 1-year subscription

Members: $195

Non-members: $335 ADD TO CART

25 downloads per 1 - year subscription

Members: $145

Non-members: $250 ADD TO CART

PURCHASE SINGLE ARTICLE

Includes PDF, HTML & Video, when available