Upconversion luminescence, visible emission on infra red (IR) excitation was achieved in a biocompatible material, fluoroapatite. Fluoroapatite crystals are well known biomaterials, which is a component of tooth enamel. Also it can be considered as an excellent host material for lanthanide doping since the ionic radii of lanthanide is similar to that of calcium ion(Ca2+) hence successful incorporation of dopants within the lattice is possible. Erbium (Er), Ytterbium (Yb) co-doped fluorapatite (FAp) nanoparticles were prepared by precipitation method. The particles show intense visible emission when excited with 980 nm laser. Since upconversion luminescence is a multiphoton process the excitation power dependence on emission will give number of photons involved in the emission of single photon. Excitation power dependence studies show that two photons are involved in the emission of single photons. The value of slope was different for different emission peak because of the difference in intermediate energy level involved. The crystal structure and morphology of the particle were determined using X-ray diffractometer (XRD) and field emission scanning electron microscope (FESEM). These particles with surface functionalisation can be used for live cell imaging.
Recently, flexible organic optoelectronics have got great attention because of their light weight, mechanical flexibility and cost effective fabrication process. Conjugated polymers like PEDOT: PSS are widely used for the transparent electrode applications due to its chemical stability, high conductivity, flexibility and optical transparency in the visible region. Conductivity of the PEDOT: PSS polymer can be enhanced by adding organic solvents or conducting nano fillers like CNT, graphene, etc. Carbon nanotubes are good nano fillers to enhance the conductivity and mechanical strength of PEDOT: PSS composite film. Inthe present work, the effect of gold nano particles in PEDOT: PSS/CNT composite is studied. The conductivity enhancement in PEDOT: PSS/CNT thin films can be attributed to the formation of CNT network in the polymer matrix and conformational change of the PEDOT from benzoid to quinoid structure. Even though the conductivity was enhanced, the transparency of the composite thin films decreased with increase in CNT concentration. To overcome this problem, gold nano particles were attached to CNT walls via chemical route. AuMWCNT/PEDOT: PSS composite films were prepared by spin coating method. TEM images confirmed the decoration of gold nano particles on CNT walls. Electrical and optical properties of the composite films were studied. This simple solution processed conducting films are suitable for optoelectronic applications
KEYWORDS: Solar cells, Solar energy, Upconversion, Near infrared, Ytterbium, Luminescence, Erbium, Scanning electron microscopy, Absorption, External quantum efficiency
The optical properties of Yb3+/Er3+ doped Y2O3 upconversion phosphor and the enhancement of efficiency of a-Si:H solar cell on incorporation of upconverter are investigated. The Y2O3 host material has high corrosion resistance, thermal stability, chemical stability, low toxicity and relatively low phonon energy (≈ 500 cm-1). Y2O3:Yb3+ (x %): Er3+ (y %) upconversion nanophosphors with different dopant concentrations were synthesized via simple hydrothermal method followed by a heat treatment at 1200°C for 12 hrs. Highly crystalline, quasi-spherical, body centered cubic Y2O3 structure was obtained. The structure, phase and morphology of the nanocrystals were determined using x-ray diffraction and SEM. Following pumping at 980 nm two dominant emission bands were observed at about 550 nm(green) and 660 nm(red), corresponding to 2H11/2, 4S3/2 → 4I15/2 and 4F9/2 → 4I15/2 transitions respectively. The dependence of emission intensity on pump power shows that the mechanism involved is two photon absorption. The upconversion phosphor along with a binder is coupled behind the a-Si:H solar cell which absorbs transmitted sub-band-gap photons and emits back the upconverted visible light which can be absorbed by the solar cell. Under suitable intensity of illumination the solar cell short circuit current is found to be increased on adding the upconversion layer.
Access to the requested content is limited to institutions that have purchased or subscribe to SPIE eBooks.
You are receiving this notice because your organization may not have SPIE eBooks access.*
*Shibboleth/Open Athens users─please
sign in
to access your institution's subscriptions.
To obtain this item, you may purchase the complete book in print or electronic format on
SPIE.org.
INSTITUTIONAL Select your institution to access the SPIE Digital Library.
PERSONAL Sign in with your SPIE account to access your personal subscriptions or to use specific features such as save to my library, sign up for alerts, save searches, etc.